Advantages Good tensile strength, flexural modulus and elongation at break with the best combination of volume resistance and dielectric strength when compared with other modified grades of DAP. Disadvantages As with other glass filled DAP mouldings, can be anisotropic with a tendency to warp. Typical Properties Property Value Density (g/cm3) 1.75 Surface Hardness RM110 Tensile Strength (MPa) 60 Flexural Modulus (GPa) 10 Notched Izod (kJ/m) 0.37 Linear Expansion (/°C x 10-5) 3.2 Elongation at Break (%) 1 Strain at Yield (%) N/A Max. Operating Temp. (°C) 160 Water Absorption (%) 0.2 Oxygen Index (%) 25 Flammability UL94 HB Volume Resistivity (log ohm.cm) 15 Dielectric Strength (MV/m) 16 Dissipation Factor1kHz 0.02 Dielectric Constant 1kHz 4.7 HDT @ 0.45 MPa (°C) 260+ HDT @ 1.80 MPa (°C) 200 Material Drying hrs @ °C 4 @ 40 Melting Temp. Range (°C) 60 - 90 Mould Shrinkage (%) 0.6 Mould Temp. Range (°C) 150 - 180
Applications Electrical connectors, relay bases, switches, coil formers and brush holders.