Advantages Higher tensile strength, flexural modulus, notched izod impact strength and lower mould shrinkage than the other modified grades of DAIP. Disadvantages Lower volume resistance, dielectric strength and higher density compared with the other modified grades of DAIP in Plascams. Typical Properties Property Value Density (g/cm3) 1.81 Surface Hardness RM112 Tensile Strength (MPa) 82 Flexural Modulus (GPa) 11.3 Notched Izod (kJ/m) 0.37 Linear Expansion (/°C x 10-5) 3 Elongation at Break (%) 0.9 Strain at Yield (%) N/A Max. Operating Temp. (°C) 180 Water Absorption (%) 0.25 Oxygen Index (%) 27 Flammability UL94 V2 Volume Resistivity (log ohm.cm) 13 Dielectric Strength (MV/m) 14 Dissipation Factor1kHz 0.012 Dielectric Constant 1kHz 4.1 HDT @ 0.45 MPa (°C) 260+ HDT @ 1.80 MPa (°C) 280 Material Drying hrs @ °C 4 @ 40 Melting Temp. Range (°C) 60 - 90 Mould Shrinkage (%) 0.2 Mould Temp. Range (°C) 150 - 180
Applications Pump impellers, tool handles, and switchgear.